WO1999006858A1 - Retroreflective article having a binder layer containing an epoxy resin and a silicone cross-linked polymer - Google Patents
Retroreflective article having a binder layer containing an epoxy resin and a silicone cross-linked polymer Download PDFInfo
- Publication number
- WO1999006858A1 WO1999006858A1 PCT/US1997/022245 US9722245W WO9906858A1 WO 1999006858 A1 WO1999006858 A1 WO 1999006858A1 US 9722245 W US9722245 W US 9722245W WO 9906858 A1 WO9906858 A1 WO 9906858A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- retroreflective
- layer
- article
- polymer
- binder
- Prior art date
Abstract
Description
Claims